MEASUREMENT OF NANOSTRUCTURED POROUS SILICON POROSITY USING NANOINDENTOR
Porous silicon (PSi) is composed by a nanocrystalline Si skeleton immersed in a network of interconnected pores. Porosity will be increase when etching time and current density increased and hardness values decrease with increase of porosity and anodization time.
Saved in:
Main Author: | |
---|---|
Format: | Thesis Book |
Published: |
Shah Alam, Selangor
University Teknology MARA. Faculty of Applied Sciences
2009
|
Subjects: | |
Online Access: | Click Here to View Status and Holdings. |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
MARC
LEADER | 00000nam a2200000#i 4501 | ||
---|---|---|---|
001 | wils-940486 | ||
005 | 2019319162551 | ||
008 | s2009 MY ag# t#000 ##ENG#D | ||
040 | # | # | |a UiTM |e rda |
041 | 0 | # | |a Eng |
090 | 0 | 0 | |a TA418.9.N35 |b N67 2009 |
100 | 0 | # | |a Noridah Nordin |e author |
245 | 1 | 0 | |a MEASUREMENT OF NANOSTRUCTURED POROUS SILICON POROSITY USING NANOINDENTOR |c NORIDAH BINTI NORDIN |
264 | # | 1 | |a Shah Alam, Selangor |b University Teknology MARA. Faculty of Applied Sciences |c 2009 |
300 | # | # | |a xi, 36 pages |b illustrations |c 30 cm |
336 | # | # | |a text |2 rdacontent |
337 | # | # | |a unmediated |2 rdamedia |
338 | # | # | |a volume |2 rdacarrier |
500 | # | # | |a UiTM X Digitization |
502 | # | # | |a Student report (BSc.)-Universiti Teknologi MARA. Faculty of Applied Sciences, 2009 |
504 | # | # | |a Includes bibliographical references (pages 299-302) |
520 | # | # | |a Porous silicon (PSi) is composed by a nanocrystalline Si skeleton immersed in a network of interconnected pores. Porosity will be increase when etching time and current density increased and hardness values decrease with increase of porosity and anodization time. |
650 | # | 0 | |a Nanostructured materials |
710 | 1 | # | |a Faculty of Applied Sciences |e issuing body |
856 | 4 | 0 | |z Click Here to View Status and Holdings. |u https://opac.uitm.edu.my/opac/detailsPage/detailsHome.jsp?tid=940486 |
998 | # | # | |a 00264#1a002.8.2||00264#1b002.8.4||00300##a003.4.1||00300##b003.6.1||00300##c003.5.1||00500##a002.17.2||00502##a007.9.2||00520##a007.2||00520##b007.2|| |