PREPARATION AND CHARACTERIZATIONS OF NANO TiO₂ POWDER

Titanium dioxide (TiO₂) powder was prepared by sol gel method using Titanium (IV) Isopropoxide (TTIP) as precursor and Ethanol (C₂HƽOH) as solvent. The result shows that the size of Titanium Dioxide (TTIP) powder was effected when used different concentration of Titanium Dioxide (TTIP)

Saved in:
Bibliographic Details
Main Author: Zainurul Atikah Zakaria (Author)
Format: Thesis Book
Published: Shah Alam, Selangor Universiti Teknologi MARA. Faculty of Applied Sciences 2011
Subjects:
Online Access:Click Here to View Status and Holdings.
Tags: Add Tag
No Tags, Be the first to tag this record!

MARC

LEADER 00000nam a2200000#i 4501
001 wils-940458
005 2019319112253
008 s2011 MY ag# t#000 ##ENG#D
040 # # |a UiTM  |e rda 
090 0 0 |a TP245.T85  |b Z35 2011 
100 0 # |a Zainurul Atikah Zakaria  |e author 
245 1 0 |a PREPARATION AND CHARACTERIZATIONS OF NANO TiO₂ POWDER  |c ZAINURUL ATIKAH BT ZAKARIA 
264 # 1 |a Shah Alam, Selangor  |b Universiti Teknologi MARA. Faculty of Applied Sciences  |c 2011 
300 # # |a xii, 50 pages  |b illustrations  |c 30 cm 
336 # # |a text  |2 rdacontent 
337 # # |a unmediated  |2 rdamedia 
338 # # |a volume  |2 rdacarrier 
500 # # |a UiTM X Digitization 
502 # # |a Student report (BSc.)-Universiti Teknologi MARA. Faculty of Applied Sciences, 2011 
504 # # |a Includes bibliographical references (pages 48-46) 
520 # # |a Titanium dioxide (TiO₂) powder was prepared by sol gel method using Titanium (IV) Isopropoxide (TTIP) as precursor and Ethanol (C₂HƽOH) as solvent. The result shows that the size of Titanium Dioxide (TTIP) powder was effected when used different concentration of Titanium Dioxide (TTIP) 
650 # 0 |a Titanium dioxide 
710 2 # |a Faculty of Applied Sciences  |e issuing body 
710 2 # |a Fakulti Sains Gunaan  |e issuing body 
856 4 0 |z Click Here to View Status and Holdings.  |u https://opac.uitm.edu.my/opac/detailsPage/detailsHome.jsp?tid=940458 
998 # # |a 00264#1a002.8.2||00264#1b002.8.4||00300##a003.4.1||00300##b003.6.1||00300##c003.5.1||00500##a002.17.2||00502##a007.9.2||00520##a007.2||00520##b007.2||